- The Relation between the Purity of Zinc and the Recrystallization Temperature (Studies of the Effect of Purity of Zinc on Its Properties, 4th Report)
- ジュンアエン ノ サイケッショウ オンド ニ ツイテ
この論文をさがす
抄録
The recrystallization temperature of refined high purity zinc (zone-refined from 99.999 pct distillated zinc) after rolling reduction, has been examined by means of X-ray analysis and of microscopic study, with three kinds of pure zinc of purities of 99.1, 99.98, 99.999 pct as controls. Hardness tests were made on these specimens cold-rolled and annealed. These hardness curves were found to show some different aspects from the ordinary curves taken on metals or alloys, cold-rolled in various degrees and then annealed at various temperatures. From such results it has been concluded that the recrystallization temperature cannot be exactly determined from these hardness-annealing curves. It was ascertained by means of X-ray analysis using low temperature camera that the recrystallization of high purity zinc began at lower temperature than that of low purity one, and that such super-purity zinc as was zone-refined from 99.999 pct distillated zinc would begin to recrystallize for 1 hr by keeping for 1 hr at about −70°C after 50 pct cold rolling, and complete at −70°C after 90 pct cold rolling, after storaging in dry ice and aceton solution at −78°C.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 23 (1), 79-82, 1959
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206482167168
-
- NII論文ID
- 130007333832
- 40018257294
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9152734
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可