- Effect of Chromium Contents on Atmospheric Corrosion of Steel in Chloride Environment
- エンカブツ ヒライ タイキ フショク カンキョウ ニ オケル ハガネ ノ タイコウセイ ニ オヨボス Cr テンカ ノ エイキョウ
この論文をさがす
抄録
The role of chromium contents on atmospheric corrosion of steel in the environment containing chloride ion was studied by exposure test and electrochemical experiments. It was found that corrosion resistance of 1% chromium steel was lower than that of the steel without chromium in the environment whose concentration of chloride ion was very high by the exposure test. On the other hand, containing chromium increases corrosion resistance in the environment with low chloride concentration. In neutral chloride solution corrosion rate of 1% chromium steel was lower than that of the steel without chromium, but was high in low pH chloride solution. The pH dependence of corrosion resistance of 1% chromium steel corresponded with the corrosion resistance by the exposure test.<br>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 77 (3), 107-113, 2013
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206482225152
-
- NII論文ID
- 10031155993
-
- NII書誌ID
- AN00187860
-
- COI
- 1:CAS:528:DC%2BC3sXntVCrsLc%3D
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 024346226
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可