- Tensile Strength, Elongation and Flow Stress of Aluminum-Magnesium Alloys under Dynamic Loading
- ショウゲキ カジュウ カ ニ オケル アルミニウム-マグネシウム ゴウキン ノ ヒッパリ ツヨサ , ノビ , ヘンケイ テイコウ ニ ツイテ
この論文をさがす
抄録
The dynamic tensile tests with strain rate 37/sec was performed at −196°C to 130°C for aluminum-magnesium alloys (0.93, 1.82 and 3.67%Mg) with the use of the apparatus of drop hammer type which was described in a previous paper. The results obtained were as follows:<BR>(1) The dynamic test resulted in a larger tensile strength than the static test, and the lower testing temperature increased the difference in tensile strength by the dynamic and static tests.<BR>(2) In the dynamic test the elongation seemed to increase with temperature, while the static test showed the minimum elongation around room temperature.<BR>(3) The dynamic test gave a larger flow stress than the static test and it was concluded that the larger flow stress observed in the dynamic test was due to the strain rate dependence of flow stress and the change of the internal structure of the specimen in the dynamic test which was different from that obtained by the static test.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 28 (8), 439-442, 1964
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206482294400
-
- NII論文ID
- 130007334001
- 40018258403
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153843
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可