- タイトル別名
-
- Effect of Heat Treatment on Magnetic Properties of Fe-Al-Mo Alloys
- Fe-Al-Mo ゴウキン ノ ジセイ ニ オヨボス ネツ ショリ ノ エイキョウ
この論文をさがす
抄録
The effect of molybdenum on the Fe3Al-FeAl phase transformation of Fe-Al alloys was studied by means of electrical resistivity measurement at high temperatures, and magnetic properties of the alloys under the various heat treatments were compared with the transformation process.<BR>The results obtained are as follows:<BR>(1) The transformation temperature from Fe3Al to FeAl phase increases at a rate of 17°∼18°C per molybdenum percent.<BR>(2) The temperature coefficient of resistivity is negative at the FeAl phase, and its absolute value increases with increasing molybdenum content.<BR>(3) The FeAl phase quenched in water sharply changes to the Fe3Al phase at a temperature around 250°C independent of the molybdenum content, and then the magnetic properties decrease.<BR>(4) The FeAl phase increases with temperature in 400°C-transformation temperature regions in which both FeAl and Fe3Al phases exist, so that the magnetic properties increase with temperature. The best is obtained in water-quenching from temperature above the transformation in case of 0% molybdenum, but from temperature about 50°C below it in case of 3∼4%. More than 80% of the maximum value are obtained in water-quenching between 500° and 600°C.<BR>(5) The magnetic properties remarkably decrease due to the formation of the Fe3Al phase at a quenching temperature below 400°C in case of 0% molybdenum, but slightly decrease in case of 2∼4%. This is believed to depent on the change of magnetic anisotropy and magnetostriction with molybdenum.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 28 (8), 461-464, 1964
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206482298496
-
- NII論文ID
- 40018258396
- 130007334010
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153836
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可