大気中におけるステンレス鋼の孔食発生に及ぼす MgCl<sub>2</sub>液膜の濃度および厚さの影響

DOI Web Site Web Site 被引用文献2件 参考文献39件

書誌事項

タイトル別名
  • Influences of Concentration and Thickness of MgCl<sub>2</sub> Solution Layer on Pit Initiation of Type 304 Stainless Steel in Atmospheric Environment
  • 大気中におけるステンレス鋼の孔食発生に及ぼすMgCl₂液膜の濃度および厚さの影響
  • タイキ チュウ ニ オケル ステンレスコウ ノ コウショク ハッセイ ニ オヨボス MgCl ₂ エキマク ノ ノウド オヨビ アツサ ノ エイキョウ

この論文をさがす

抄録

<p>This paper aimed to investigate conditions for pit initiation on type 304 stainless steel under MgCl2 solution layer in atmospheric environment using a CCD camera system and a surface potential measurement equipment. A droplet of dilute MgCl2 solution was put on the specimen. The specimen was set in the chamber with a relative humidity of 33% in order to make the droplet dry into the layer. The CCD camera system was employed to observe the change in the shape of the droplet and in the specimen surface during the drying process. In addition, the surface potential measurement equipment was applied for monitoring the surface potential of the specimen with the layer. When the droplet of dilute solution became thin and saturated, pitting corrosion occurred and the surface potential rapidly lowered. By contrast, thick and saturated layer did not induce pitting corrosion and the surface potential indicated the relatively low and steady. Therefore, it was revealed that the atmospheric corrosion occurred on the steel under saturated MgCl2 solution layer whose thickness less than 0.2 mm.</p>

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 81 (3), 115-119, 2017

    公益社団法人 日本金属学会