Static Globularization and Grain Growth Behavior of Ti-5Al-2Sn-2Zr-4Cr-4Mo（Ti-17） Alloy Under Static Heat Treatment Process

DOI Web Site Web Site 19 References
  • Yamane Gen
    Department of Advanced Materials Science, Faculty of Engineering, Kagawa University
  • Matsumoto Hiroaki
    Department of Advanced Materials Science, Faculty of Engineering, Kagawa University

Bibliographic Information

Other Title
  • Ti-5Al-2Sn-2Zr-4Cr-4Mo（Ti-17）合金の静的熱処理 過程の粒成長および静的球状化
  • Ti-5Al-2Sn-2Zr-4Cr-4Mo (Ti-17)ゴウキン ノ セイテキ ネツ ショリ カテイ ノ ツブ セイチョウ オヨビ セイテキ キュウジョウカ

Search this article

Abstract

<p>Grain growth behavior and static globularization behavior of the Ti-5Al-2Sn-2Zr-4Cr-4Mo(Ti-17) alloy (with the lamellar starting microstructure and the equiaxed-grained-microstructure) under static heat treatment process were investigated in this work. Rapid grain-growth and static globurarization are exhibited in the 1123HR specimen (with the equiaxed starting microstructure) rather than the lamellar specimen, which is mainly due to the quite difference in fraction of Burgers orientation relationship (BOR) (with coherent relationship) between α and β phases. The interface energy of γαβ at BOR was estimated to be approximately 0.01 J/m2 according to Lifshitz-Slyozov-Wagner(LSW) model. Static globularization behavior of the 1123HR specimen is reasonably explained in relation to the Johnson-Mehl-Avrami-Kolmogorov (JMAK) model. Here, similar apparent activation energies were exhibited for both behaviors of grain growth and globularization, indicating the similar rate-limiting mechanism for both these behaviors.</p>