- Relationships between Spark Plasma Sintering Temperature and Mechanical Properties of Combustion-Synthesized α- and β-SiAlON
- ネンショウ ゴウセイ サレタ a-オヨビ v-SiAlON ノ SPS ショウケツ オンド ト キカイテキ セイシツ ノ カンケイ
- Relationships between Spark Plasma Sintering Temperature and Mechanical Properties of Combustion-Synthesized α- and β-SiAlON
この論文をさがす
抄録
Combustion-synthesized Y-α-SiAlON and Ca-α-SiAlON powders have been consolidated by Spark Plasma Sintering (SPS) at 1300-1450℃ for 10 min, and the mechanical properties of the consolidated bulk samples were investigated. XRD analysis revealed that α-SiAlON partially transforms into β-SiAlON during the SPS and a bulk of α/β-SiAlON mixture was obtained. The fraction of β-SiAlON increases with the increase in sintering temperature and the α to β transformation ratio is high for Y-α-SiAlON compared with Ca-α-SiAlON. The hardness of the consolidated bulk increases with sintering temperature and after reaching the peak at 1350℃ the hardness gradually decreases with temperature in both the cases of Y-α-SiAlON and Ca-α-SiAlON. The increase in hardness with temperature arises from increase in density of the sintered body, while the decrease in hardness results from grain growth due to high temperatures. The fracture toughness monotonically increases with temperature and does not show a peak for both SiAlONs, although Y-α-SiAlON always exhibits higher toughness than Ca-α-SiAlON. The higher toughness of the Y-α-SiAlON is attributable to its higher fraction of transformed β-SiAlON, because the elongated shape of β-SiAlON leads to prevention of crack propagation.<br>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 79 (4), 191-194, 2015
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206482497920
-
- NII論文ID
- 130005061068
-
- NII書誌ID
- AN00062446
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- HANDLE
- 2115/75374
-
- NDL書誌ID
- 026302490
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可