- Investigation of the Ti-rich Ti-Fe-Mn Alloy System (2nd Report). On the Liquidus Surface of the Ti-Fe-Mn System
説明
The liquidus surface of the Ti-Fe-Mn system was determined by melting point determination, microscopic observation and Micro-Vickers hardness measurement. Summing up the present experimental results, the liquidus surface diagram as shown in Fig. 2 was obtained. In the figure, AE1EE2 represents a field of the primary separation of Ti and those of TiMn, TiFe and Ti(Fe, Mn)2 are respectively shown by E1EPP1 E2EPP2 and BP1PP2CE3F. The Ti(Fe, Mn)2 phase is a continuous solid solution which exists in the wide range of composition between TiFe2 phase in the Ti-Fe binary system and TiMn2 phase in the Ti-Mn binary system. In this ternary system, two invariant reactions & liquid+Ti(Fe,Mn)_2 \ ightleftharpoonsTiFe+TiMn at about 1,100°, <BR> & liquid \ ightleftharpoonsTi+TiFe+TiMn at about 1,050°are considered to exist.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 22 (5), 265-269, 1958
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206482520704
-
- NII論文ID
- 130007334191
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可