フェロマンガン鉱滓の電気伝導度について

DOI Web Site Web Site

書誌事項

タイトル別名
  • On the Electrical Conductivity of Ferro-Manganese Slags
  • フェロ マンガン コウシ ノ デンキ デンドウド ニ ツイテ

この論文をさがす

抄録

The electrical conductivity of the MnO-CaO-SiO2-Al2O3 system at the composition range 5∼25%MnO and 0.78∼1.43CaO/SiO2 was measured, and the following results were obtained. (1) The specific conductivity “κ” of the 6%Al2O3 samples is 0.1∼0.36 Ω−1·cm−1 at 1,400°C. It increases with a rise of temperature, and at the same basicity, increases with the ratio of the MnO content. When the content of MnO is constant, the conductivity increases with CaO/SiO2, but when this ratio, i.e. the basicity, is above 1.12, it decreases with the increase of CaO/SiO2. (2) From the results at 6%Al2O3 constant, the isoelectrical conductivity lines were plotted on the diagram of CaO-MnO-SiO2 system. (3) Within the range of Al2O3: 1.5∼15%, “κ” tends to attain the largest value at 6∼10%Al2O3. (4) From the relation between logκ and 1⁄T, it was confirmed that the conduction is ionic, and the activation energy was calculated.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 22 (3), 114-117, 1958

    公益社団法人 日本金属学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ