- High-Temperature Creep of Nickel-Tungsten Alloys (On the Relation between High-Temperature Creep and Diffusion in Nickel-Base Solid Solutions. VI)
- Ni-W ゴウキン ノ コウオン クリープ
この論文をさがす
抄録
Tensile creep properties of nickel-tungsten alloys containing up to about 10 at% of tungsten have been studied. Tests were carried out in argon atmosphere over the temperature range from 750° to 1200°C, and the stress range from 1.4 to 9 kg/mm2. Steady state creep rate (\dotεs) decreases with the increasing tungsten content. Temperature and stress dependences of steady state creep rate were analysed using Dorn’s equation, \dotεs=Cσnexp(−Qs⁄RT). Activation energies (Qs) are independent of applied stresses. They increase with the tungsten content from 66 kcal/mol for pure nickel to the maximum value of 84 kcal/mol for the alloy of 5 at%-tungsten, before they decrease with further increase of the tungsten content. Stress exponents (n) increase extremely with the tungsten content from a value of 5.0 for pure nickel to the maximum value of 7.2 for the alloy of 1.7 at%-tungsten. Whereas, in alloys containing more than this concentration of tungsten they decrease with the increasing content of tungsten to values less than that for pure nickel.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 28 (6), 304-307, 1964
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206482584064
-
- NII論文ID
- 130007334275
- 40018258372
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153812
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可