- Effect of Annealing on Properties of Sintered WC-Co Alloys
- WC-Co ゴウキン ノ セイシツ ニ オヨボス ショウドン ノ エイキョウ
この論文をさがす
抄録
WC-Co alloys having 5∼25%Co and various carbon contents were vacuum-sintered and subsequently vacuum-annealed at 600°∼800°C for about up to 50 hr. Some properties of the sintered alloys affected by the annealing were studied noticing their carbon content. Results obtained are summarized as follows:—(1) After annealing, the hardness of alloys does not change; the rupture-strength decreases associated with the slight increase of hardness of binder phase; the lattice constant of the binder, and specific resistivity of the alloys decrease; the microstructure of the binder and its stability for acidic solutions change. (2) These changes in properties result from the precipitation of W atoms from the binder phase during annealing. (3) This is a reason why the properties of the alloys having a lower content of carbon, viz, a higher dissolved W in the binder phase, change remarkably.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 28 (5), 287-291, 1964
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206482587648
-
- NII論文ID
- 40018258364
- 130007334282
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153804
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可