- Causes and Prevention of Surface Fissures on Hot-worked Steel Products (3rd Report). On the Enrichment of Tramp Elements on the Surface Layers of Steel by Oxidization while Heating
- コウザイ ノ カネツ ジョウケン ト tramp elements ノ ヒョウメン フカ
この論文をさがす
抄録
The distribution of tramp elements in the enriched layer and the scales produced by oxidization while heating was minutely investigated by spectrographic and chemical analyses. The results obtained were as follows:—(1) When steel is heated in oxidizing atmosphere, Cu, Sn, Ni, As and S contained in steel are enriched on the surface of steel. (2) A linear relationship is observed to exist between the depth from the surface of steel and the logarithm of the concentration of each enriched element contained in the layer. (3) In the case the scaling loss of steel is constant, the surface concentration of enriched Cu and Sn is decreased while that of S is increased with rising h ating temperature, and the surface enrichment of each element is also affected by the oxidizing velocity and the coexisting elements. (4) The diffusion constants of Cu and Sn in steel are determined by measurement of the enriched depth at various temperatures, and the following were the values obtained: & D_Cu^- 12700 exp(-48700/RT) cm^2/day <BR> & D_Sn^- 4570 exp(-45600/RT) cm^2/day(5) The concentrations of Cu and Sn in scales are less than those in the steel matrix, and usually depend on the degree of scaling loss.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 22 (12), 640-644, 1958
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206482779136
-
- NII論文ID
- 130007334548
- 40018257274
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9152714
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可