- Changes of Structure in α+β Brass (58.0∼62.0%Cu) by Hot-Working (On the Fundamental Studies of the Homogenious Structure in α+β Brass, 1st Report)
- アルファ ベータ オウドウ ノ ネツカン カコウ ニ オケル ソシキ ヘンカ
- Changes of Structure in α+β Brass (58.0∼62.0%Cu) by Hot-Working (On the Fundamental Studies of the Homogenious Structure in α+β Brass, 1st Report)
この論文をさがす
抄録
In this report, the changes of structure in α+β brass by hot-working temperature and working reduction were investigated using plate specimens of 58.5%Cu, 59.0%Cu, 60.0%Cu, 60.5%Cu, 61.0%Cu, 61.5%Cu and 61.9%Cu brass, of the size of 30 mm×90 mm×180 mm, and the structure after forging for various holding times using specimens of the same contents 1 cm3 in size. The results obtained were as follows: (1) There was a suitable temperature zone for producing homogenous structure in α+β brass. (2) There was a suitable holding time correlated with the hot-working temperature and the size of the specimen. (3) Within temperature zone of adapted for producing homogenous structure, it grew finer in the case of larger working reduction at the beginning.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 25 (3), 205-209, 1961
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206482821376
-
- NII論文ID
- 130007334609
- 40018257882
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153322
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可