- Effect of Carbon Contents on Corrosion Resistance and Mechanical Properties of Ni-Mo Alloys
- Ni-Mo ゴウキン ノ タイショクセイ オヨビ キカイテキ セイシツ ニ オヨボス C ノ エイキョウ
この論文をさがす
抄録
Effect of carbon contents on the properties of Ni-Mo alloys has been investigated by hardness, tensile, microscopic and corrosion tests. The corrosion tests were carried out on specimens in boiling 20%HCl for 24 hours. The following results have been obtained. (1) With increasing content of carbon, both the weight loss by corrosion and the hardness of solution-treated Ni-Mo alloys have been increased, but the elongation was lowered. This may be attributable to the increase of the eutectic carbide (M6C, a=11.09 Å), the amount of which increased by addition of carbon. (2) When air-cooled from annealing temperature of 700°C, the elongation decreased rapidly, and the higher the carbon contents, the more appreciably deteriorated the corrosion resistance due to the continious precipitation of M6C (a=10.92 Å) on grain boundaries.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 25 (6), 406-410, 1961
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206482851200
-
- NII論文ID
- 130007334655
- 40018257937
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153377
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可