高マンガン・アルミニウム青銅に対する諸性質と冷却速度について

DOI Web Site Web Site

書誌事項

タイトル別名
  • Effects of Cooling Rate on the Properties of High-Manganese-Aluminium Bronze
  • コウマンガン アルミニウム セイドウ ニ タイスル ショ セイシツ ト レイキャク ソクド ニ ツイテ

この論文をさがす

抄録

In our previous report (Effect of Nickel, Iron and Manganese Addition on β→α+γ2 Transformation of Cu-Al Alloys), adding Mn to Al-bronze containing β phase was effective to stabilize β phase and depress the so-called self-annealing phenomenon. Based on that result, this experiment was carried out to decide the region free from γ2-precipitate which caused self-annealing in Cu-Al-Mn system. The microstructures and hardness of Cu-Al-Mn alloys containing 5∼12%Al and 4∼12%Mn, water quenched or treated at various cooling rate as 1, 0.15 and 0.02°C/min, was examined and noted in diagrams. Then the mechanical tests of Cu-9.5%Al-Mn and Cu 8%Al-Mn alloy castings containing various Mn amount were carried out on tensile strength, elongation and impact-value. The results obtained are summarized in the following: The microstructures of high Mn-Al-bronzes containing above 6 wt%Mn consist of α,β and Cu3Mn2Al phases and free from the precipitation of γ2 and it was suggested they show excellent mechanical properties even when slowly cooled, say, at 0.02°C/min.In the results of mechanical test, Cu-Al-Mn alloy containing β phase showed an increase of tensile strength and a slight decrease of elongation with the increase in Mn wt%, but did not show self-annealing when containing high Mn content.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 25 (6), 397-401, 1961

    公益社団法人 日本金属学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ