- Influence of Two-Step Aging on Cluster Formation and Tensile Property in Al-Mg-Si Alloy
- Al-Mg-Si ゴウキン ニ オケル 2ダン ジコウ ノ クラスタ ケイセイ ト キカイテキ セイシツ エ ノ エイキョウ
この論文をさがす
説明
The change of the state of Mg-Si cluster with aging time at 303 K and 323 K after pre-aging at 363 K was studied by means of tensile test focusing on yield stress, 3DAP (3 Dimensional Atom Probe) and DSC (Differential Scanning Calorimetry) measurement. Mg-Si clusters formed during isothermal aging at the temperature of 363 K after solution treatment were different from the ones formed at the temperatures of 303 K and 323 K. During aging at 303 K and 323 K following pre-aging at 363 K, the cluster that was once formed at 363 K grew in size together with the new nucleation of another type of cluster formed at 303 K and 323 K. The increment of yield stress with aging time at 303 K and 323 K after pre-aging at 363 K was greater than the one without pre-aging at 363 K. This was considered to stem from the fact that the cluster formed during pre-aging at 363 K further grows during aging at 303 K and 323 K but at the same time the another type of cluster is supposed to newly nucleate and grow at 303 K or 323 K after pre-aging, both of which are inferred to contribute to the larger increase in yield strength.<br>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 76 (12), 677-683, 2012
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206482881152
-
- NII論文ID
- 10031129957
-
- NII書誌ID
- AN00187860
-
- COI
- 1:CAS:528:DC%2BC3sXit1ertrg%3D
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 024135464
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可