On the Creep Rupture Properties of 18-8 Ti Stainless Steel Tube. (Creep Rupture Properties of 18-8 Ti Stainless Steel, 1st Report)
Bibliographic Information
- Other Title
-
- 18-8Ti型ステンレス鋼管材のクリープ破断特性について
- 18-8Tiガタ ステンレス コウカンザイ ノ クリープハダントクセイ ニ ツイテ
Search this article
Abstract
Investigations of the effect of the grain size, working, and heat treatment on the creep rupture properties of 18-8 Ti stainless steel tube have been carried out. As the result of 650°C creep rupture tests on the tube material, the following conclusions have been reached. (1) It is generally recognised that, in the case of the tube material having fine grain structure, the creep rupture strength is small and the rupture elongation is large. However, our studies indicate that the grain size has not much bearing upon the creep rupture properties. (2) After working, the creep rupture strength in the short-period side becomes large, but at the long period side, it becomes considerably small and the rupture elongation increases. Such a tendency becomes more pronounced in the case of cold working than in hot working. (3) Heat treatment after working has a great effect upon the creep rupture properties. Just simple annealing for softening makes the creep rupture properties worse than those of the material which was subjected to working only. The material will have the better creep rupture properties by being treated at a temperature whithin the range where the maximum possible amount of C and Ti are dissolved as super-saturated solute elements.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 25 (4), 238-241, 1961
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390001206482896640
-
- NII Article ID
- 130007334730
- 40018257898
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 9153338
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed