- Ferromagnetic Domain Patterns on Two-Phase Nickel-Cobalt Alloy and Pure Cobalt Crystals (Ferromagnetic Domain Patterns on Ni-Co Alloy and Pure Cobalt Crystals, II)
- 2ソウ Ni-Co ゴウキン オヨビ ジュンCo ケッショウ ノ ジク モヨウ
この論文をさがす
抄録
Ferromagnetic domain patterns were observed, using the powder pattern technique, with single crystals of Ni-Co alloys containing 69 and 70%Co as well as with cobalt ingots as solidified slowly and then variously heat-treated. In 69%Co-Ni single crystals, ε (hexagonal close-packed) phase crystals were seen as layers parallel to {111} planes, indicating that the boundary of the γ (fece-centered cubic) phase is located at 68%Co. On the {110} surface of 69%Co-Ni single crystals, traces of ε phase crystals were seen as bands parallel to two ⟨112⟩ and one ⟨110⟩ directions. The behavior of 180°C domain walls in the matrix γ phase crystals when they cross the ε-phase crystal bands show that the direction of easy magnetization in ε phase nickel-cobalt alloys is [0001] direction, irrespective of the composition, just as in cobalt. Cobalt specimens, which were solildfied slowly from the melt and then cooled very sowly through the γ→ε transformation temperature, are seen to be divided finely by numerous ε-phase crystal bands, among which there exist γ-phase cryistal regions of parallelogram and triangular shapes. A similar structure is observed in cobalt as quenched in hot water after slow solidification, although the proportion of γ-phase in quenched specimens is larger than in slowly cooled specimens.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 25 (3), 229-233, 1961
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206482897664
-
- NII論文ID
- 130007334732
- 40018257876
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153316
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可