- Annealing Textures of Cold-Rolled Fe-Si-Al Alloys
- ケイソ-アルミニウムテツ レイカン アツエンバン ノ サイケッショウ シュウゴウ ソシキ
この論文をさがす
抄録
Several Fe-Si-Al alloys containing 3 wt.%Si plus Al (including 3 wt.%Si-Fe and 3 wt.%Al-Fe alloys) were prepared by melting in air in an induction furnace. After forging and annealing, they were processed in two cold-rolling operations separated by an intermediate annealing. The following two combinations of the cold-rolling reductions and the annealing conditions were tested: (G) 65% reduction,annealing at 850°C for 1 hr in vacuum, 65% reduction, final annealing at 1050°C for 1 hr in vacuum. (W) 80% reduction, annealing at 1000°C for 1 hr in H2, 80% reduction, final annealing at 1000°C for 2 hrs in H2. The final annealing textures were examined by magnetic torque measurements and by X-ray pole-figure determinations. The following results have been obtained. (1) In all specimens, larger cube/Goss ratio in the final annealing texture was obtained by the W-process. Especially, larger cube/Goss ratio was obtained in alloys containing more than 1.2%Al. (2) The Goss texture was developed by the G-process and the effect of the inclusion inhibition on the sharpness of the Goss texture was not appreciably different in any of the specimens.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 25 (11), 712-716, 1961
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206483175040
-
- NII論文ID
- 40018257828
- 130007335123
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153268
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可