- Relation of Isothermal Heating Versus Magnetostriction and Young’s Modulus of Hot-Rolled “Alfer” Sheet
- コウオン アツエン サレタ アルフェル ゴウキン ノ トウオン カネツ ト ジワイ オヨビ ヤング ダンセイリツ ノ カンケイ
- Relation of Isothermal Heating Versus Magnetostriction and Young’s Modulus of Hot-Rolled “Alfer” Sheet
この論文をさがす
抄録
The change of magnetostriction and Young’s modulus of hot-rolled “Alfer” sheets, quenched in water and then subjected to heating cycles of one minute heating followed by air cooling at 300°, 400°, 500°, and 600°C were studied. The saturation magnetostriction increased abruptly at the initial step of heating time except at 300°C, and the tendency of the increase was the sharpest at 500°C, sharper at 600°C, and gentle at 400°C. All the specimens showed a distinct maximum at 500°C. The saturation magnetostriction in 45° direction showed a clear two-step variation at 400°C run. The change in Young’s modulus with heating time showed two different tendencies: (A) the young’s modulus decreases to a minimum, then increases to a maximum, and then decreases again; (B) the modulus gradually falls to a constant level. In 500° and 600°C process, the Young’s modulus in 45° direction of A·F-2 specimen (1 mm in thickness) showed abnormal change, and increased to a maximum and then decreased.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 25 (12), 754-758, 1961
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206483185280
-
- NII論文ID
- 40018257853
- 130007335145
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153293
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可