- Fundamental Studies on the Homogenous Structure in α+β Brass; (II, Changes of Structure in α+β Brass at High Temperature Observed by High-Temperature Microscope)
- コウオン ケンビキョウ ニ ヨル アルファ ベータ オウドウ ノ カネツ トチュウ ノ ソウヘンカ
- Fundamental Studies on the Homogenous Structure in α+β Brass; (II, Changes of Structure in α+β Brass at High Temperature Observed by High-Temperature Microscope)
この論文をさがす
抄録
Specimens of α+β brass of 59.98%Cu, of 3 mm×10 mm×10 mm size cut out from an ingot of 30 mm×90 mm×180 mm size and polished but not etched were studied under a high-temperature microscope, to examine continuously the changes in structure under elevated temperature, beginning at room temperature and rising to 780°C. The results obtained were as follows: (1) Unevenness appeared in the β-grains at 400∼550°C, while the α-grains grew larger, the volume of α feaching the maximum at 550°C (2) α began to be absorbed by β in the vicinity of 600°C (3) At constant temperature, the larger was the absorption of α by β, the longer the holding time, and the absorption was the larger, the higher the temperature. (4) In the β-monophase range under high temperature, new β-grain boundaries were formed crossing the original boundaries, and while making vehement translocations, steadily went on stabilizing.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 25 (11), 685-688, 1961
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206483221632
-
- NII論文ID
- 130007335207
- 40018257834
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153274
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可