- Phase Translation in Isothermally Heated Hadfield Steel at 500°, After Solution Treatment
- ヨウタイカ ショリ シタ コウMn コウ ノ 500 コウオン カネツ ニ ヨル ソウヘンカ
- Phase Translation in Isothermally Heated Hadfield Steel at 500°, After Solution Treatment
この論文をさがす
抄録
Hadfield steels, isothermally heated at some temperatures, precipitates grain-boundary carbides, platelet carbides and pearlitic constituents. In steels, with the precipitates grown up to large quantity, γ was transformed to ε at about room temperature in cooling, then the ε phase was present with carbides and α in steels. The equilibrium phases of Hadfield steels at room temperature were reported as α+carbide, but the process of phase translation leading to equilibrium is not yet known. In this works, standard Hadfield steels of chemical composition of C 1.2%, Mn 13.71% and isothermally heated at 500° for various durations after solution treatment, were studied mainly dilatometrically and magnetically. At 500°, the γ-phase in this steel was primarily translated to (γ+c), next to (γ+α+c) to (α+c) and to the final equilibrium phase (α+c). But it required a very long time to attain the equilibrium phase. At room temperature, the γ-phase in this steel primarily translated to (γ+c), then to (γ+α+c), to (γ+ε+α+c), to (ε+α+c), to (α+c), and to finally to the equilibrium phase (α+c). The ε-phase in Hadfield steel is apparently a metastable phase which appears in phase translation process to equilibrium.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 25 (1), 61-65, 1961
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206483233408
-
- NII論文ID
- 130007335229
- 40018257799
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153239
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可