The Residual Stresses of 1%C Steel and 1%C, 1%Cr and 1%Mo Steel by Quenching, Subzero Quenching and Tempering
Bibliographic Information
- Other Title
-
- 1%C鋼および1%C, 1%Cr, 1%Mo鋼の熱処理による残留応力
- 1 C コウ オヨビ 1 C , 1 Cr , 1 Mo コウ ノ ネツ ショリ ニ ヨル ザンリュウ オウリョク
Search this article
Abstract
The residual stresses in the two commercial steels after water,oil and subzero quenching and tempering were studied. The steels containing 1%C, and 1%C, 1%Cr and 1%Mo were used. The form and dimension of residual stresses were decided almost according to the thermal career from heating temperature of hardening to room temperature, and not affected by subzero treatment while the hardness was decidedly increased. A marked decrease of residual stresses was seen by the decomposition of retained austenite but they did not disappear completely even by tempering at 550°C for 1 hours.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 25 (10), 618-622, 1961
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390001206483243520
-
- NII Article ID
- 40018257801
- 130007335251
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 9153241
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed