- On Corrosion Resistivity of Heat Treated 17-7 PH. Stainless Steel Containing About 1%Al (Study on 17-7 PH Stainless Steel (5))
- ヤク 1 Al オ ガンユウ スル 17-7PH フシュウコウ ネツ ショリザイ ノ タイショクセイ ニ ツイテ
この論文をさがす
抄録
17%Cr-7%Ni stainless steel containing 0.93%Al was used for the experiments of acid corrosion resistance after several heat treatments such as solution treatment at 1050°, cooling from 750∼800°C in water or air and aging at 400∼500°C for 0.5∼500 hr. As corrosion reagents, 10 wt% sulphuric acid (30°C) and 40 wt% nitric acid (boiling) solutions were used. The following results were obtained; (1) Against 10 wt% sulphuric acid solution, this steel aged at a lower temperature than that for obtaining max. mechanical properties showed as strong corrosion resistivity as 18-8 stainless steel. Specimens heat-treated under such desirable condition attained a passive state in the soaking time up to 12 hr. (2) Against 40 wt% boiling nitric acid solution, this steel heat-treated under suitable conditions shows corrosion resistivity superior to that of 18-8 stainless steel.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 25 (1), 23-26, 1961
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206483260672
-
- NII論文ID
- 130007335288
- 40018257798
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153238
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可