- The Effect of Cold-Drawing and Annealing on the Rigidity Modulus and Internal Friction in Stainless Steel Wires
- フシュウコウセン ノ カコウ オヨビ ショウドン ニ ヨル ゴウセイリツ , ナイブ マサツ ナド ノ ヘンカ ニ ツイテ
この論文をさがす
抄録
The changes of the rigidity modulus, the electrical resistivity, the hardness and the internal friction due to cold drawing and annealing were measured in 13Cr- and 18-8 stainless steel wires. The measurements were made on specimens of 0.7 or 0.6 mm diameter, using a torsion pendulum, a potentiometer and a micro-Vicker’s hardness tester. The results obtained were as follow: (1) The rigidity modulus of 13Cr stainless steel wire decreased slightly by the cold drawing above 30% in area reduction. (2) The internal friction of 13Cr stainless steel wire decreased remarkably by cold drawing of less than 10% reduction in area, but gradually increases by the drawing above 10% reduction. (3) The internal friction of 18-8 stainless steel wire increased remarkably with the amount of cold drawing less than 3% in reduction in area, but gradually increased by the drawing above 3% reduction. (4) The rigidity modulus of 13Cr- and 18-8 stainless steel wire increased slightly by annealing at a temperature higher than 150°. (5) The internal friction of 13Cr stainless steel wire decreased remarkably by annealing at 100∼300° after cold drawing, but increased at 400∼650°. (6) The internal friction of 18-8 stainless steel wires cold-drawn less than 22% in reduction in area decreased gradually by annealing at 100∼650°, but that of the wires cold drawn more than 49% in reduction decreased remarkably by annealing at 100∼250°, and increased by annealing at 550∼650°.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 25 (1), 30-33, 1961
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206483262720
-
- NII論文ID
- 130007335292
- 40018257797
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153237
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可