- Nonmagnetic Elinvar-Type Alloys in Mn-Cu-Cr System
- Mn-Cu-Crケイ ヒジセイ エリンバーカタ ゴウキン ニ ツイテ
この論文をさがす
抄録
Measurements of Young’s modulus at −150°∼400°C and of thermal expansion, rigidity modulus and hardness at room temperature have been carried out with Mn-Cu-Cr alloys subjected to a variety of heat treatment and cold-working. It was found that Mn-Cu-Cr alloys containing about 5.0∼56.0%Cu and 0.1∼24.0%Cr slow-cooled after heating for 1 hr at 950°C showed a minimum in Young’s modulus-temperature curves and its anomaly may be a antiferromagnetic Néel points. The values of Young’s modulus at room temperature in the annealed state were higher than those in the cold-worked or water-quenched state, the difference becoming remarkably large with increasing manganese or chromium content. The temperature coefficient of Young’s modulus showed a wide variation by annealing, water-quenching, cold-working and reheating after water-quenching or cold-working, and also with alloy composition. It is also to be noted that the temperature coefficients of Young’s modulus as a function of composition exhibited a large maximum and minimum in positive and negative signs, thus showing the Elinvar property. The variation in rigidity modulus and its temperature coefficient by heat treatment, cold-working and composition showed a close resemblance to that in Young’s modulus and its temperature coefficient. The hardness in the annealed, cold-worked and water-quenched states were generally lower than that in the reheated state after cold-working or water-quenching. Further the oxidation and corrosion resistance properties of Mn-Cu-Cr alloys were superior to binary alloys in Mn-Cu and Mn-Ni.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 35 (12), 1150-1155, 1971
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206483420160
-
- NII論文ID
- 40018257115
- 130007335456
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 8372429
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可