Changes in Eutectic Structure and Apparent Viscosity by Stirring of Solidifying Al-Al<SUB>3</SUB>Fe and Al-Si Eutectic Alloys
-
- Miwa Kenji
- Nagoya Institute of Technology
-
- Ohashi Teruo
- Nagoya Institute of Technology
-
- Fukusako Tatsuichi
- Osaka University
Bibliographic Information
- Other Title
-
- Al-Al<SUB>3</SUB>FeおよびAl-Si共晶合金の凝固時の撹拌による共晶組織およびみかけ粘性の変化
- Al-Al3FeおよびAl-Si共晶合金の凝固時の攪拌による共晶組織およびみかけ粘性の変化
- Al Al3Fe オヨビ Al Si キョウショウ ゴウキン ノ ギョウコジ
Search this article
Abstract
Off-eutectic Al-1.5 mass%Fe alloys have been stirred rotationally at the rates from 0.83 s−1 to 12.5 s−1 in a partially solidified state, and variations of eutectic structures and apparent viscosity have been studied. Furthermore, Al-Al3Fe eutectic alloys have been solidified unidirectionally with stirring, and the effect of stirring on the growth morphology of the solidification front has been studied. Al-Si eutectic alloys have been also studied with the same procedure. Component phases in the Al-Al3Fe eutectic are separated by stirring in a partially solidified state. The apparent viscosity of Al-1.5 mass%Fe alloys decreases temporarily in the beginning of the eutectic reaction at most stirring rates. Eutectic Al3Fe grows as a leading phase at the solidification front without stirring, but eutectic α phase partly grows dendritically and becomes a leading phase by stirring. Then eutectic Al3Fe phases form primarily in a residual liquid. The dendritic and leading α phase covers the solidification front more widely with increase in stirring rate. The effect of stirring on the growth morphology of the solidification front in the Al-Si eutectic alloys is similar to that of the Al-Al3Fe eutectic alloy.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 49 (11), 1002-1008, 1985
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001206483682816
-
- NII Article ID
- 130007335922
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 3058166
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed