- Damping Capacity of Gentalloy in the Fe-W System
- Fe Wケイ ゴウキン Gentalloy ノ ゲンスイノウ ニ ツイテ
この論文をさがす
抄録
Measurements of the internal friction Q−1 and mechanical properties have been carried out on open-melted Fe-W alloys containing 0∼20%W. The highest Q−1 value of 34×10−3 at room temperature is obtained with an Fe-14%W alloy rapid-cooled after heating at 1200°C for 1 h. The Q−1 value measured at temperature T increases with increasing T, and shows a minimum near T⁄Tc=0.7 (Tc: magnetic transformation temperature). If a static magnetic field H is applied to the specimen, Q−1 shows a two-step decrease with increasing H. The variations of Q−1 and the coercive force Hc with composition and/or heat-treatment are opposite to each other, i.e. the alloys having larger Q−1 exhibit smaller Hc. The mechanical strength of the alloys increases considerably with the W content.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 42 (12), 1134-1137, 1978
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206483687040
-
- NII論文ID
- 130007335929
- 40002873990
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 1974032
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可