Redox Equilibria in Wustite Doped with CaO, SrO and BaO

DOI Web Site Web Site 1 Citations
  • Iguchi Yoshiaki
    Department of Metallurgical Engineering, Nagoya Institute of Technology
  • Kubokoya Ryoji
    Graduate Student, Nagoya Institute of Technology
  • Hirao Jiro
    Department of Metallurgical Engineering, Nagoya Institute of Technology

Bibliographic Information

Other Title
  • CaO, SrO, BaOを固溶したウスタイトの酸化還元平衡
  • CaO,SrO,BaO オ コヨウシタ ウスタイト ノ サンカ カンゲン ヘイ

Search this article

Description

This study was performed to obtain the concentration of defects and the activities of components in wustite doped with MeO(Me: Ca, Sr and Ba). The composition as FeO-Fe2⁄3O-MeO for wustite in equilibrium with CO-CO2 gas mixtures of PCO<SUB>2</SUB>⁄PCO=30⁄70, 50⁄50 and 60⁄40 at each temperature of 1273, 1373 and 1473 K, was determined by an analysing method utilizing the weight loss during reduction. The concentration of cation vacancy (VFe\varparallel) is estimated as one-third of the mole fraction of Fe2⁄3O. The value of (VFe\varparallel) increases with an increase in the amount of MeO and in the ionic radius of Me except for the higher concentrations of CaO. The increase in the value of (VFe\varparallel) may be interpreted qualitatively by considering that the strain generated due to the difference in radius in the substitutional dissolution of MeO can be relieved by the formation of an association [MeFe×·VFe\varparallel]. Furthermore, the activities of FeO and MeO were estimated by Schumann’s method from the oxygen pressure contours for wustite doped with CaO at 1273 K.

Journal

Citations (1)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top