書誌事項
- タイトル別名
-
- Damping Capacity of Fe-Mo Alloys
- Fe Mo ゴウキン ノ ゲンスイノウ ニ ツイテ
この論文をさがす
抄録
The measurements of internal friction Q−1 and mechanical properties have been carried out for open-melted Fe-Mo alloys containing 0∼16%Mo. The Q−1 values linearly increase with the maximum shear strain amplitude εm and decrease after reaching a peak at εm=about 1.2×10−4. This peak heights gradually diminish with increasing tensile load. The Q−1 values are as small as 0.5×10−3 in the cold-worked state, while they are considerably large in the annealed state and increase with annealing temperature. The highest Q−1 value of 58×10−3 is obtained with an Fe-6%Mo alloy annealed at 1200°C for 1 h.<BR>The results obtained indicate that Q−1 increases with measuring temperature and decreases rapidly with external magnetic field. The fairly large value of Q−1 in these alloys are mainly due to the effect of magnetomechanical hysteresis. The mechanical strengths of Fe-Mo alloys increase with Mo content, for example, an Fe-6%Mo alloy shows a tensile strength of 390 MPa and a yield strength of 200 MPa, an elongation of 29% and Vickers hardness 135, when subjected to annealing at 1000°C for 1 h.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 41 (8), 820-823, 1977
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206483742464
-
- NII論文ID
- 130007336030
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 1840910
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可