冷間引抜鋼丸棒の残留応力

書誌事項

タイトル別名
  • Residual Stress in Cold Drawn Carbon Steel Bar
  • レイカン ヒキヌキ コウマルボウ ノ ザンリュウ オウリョク

この論文をさがす

説明

Residual stresses in 0.25% carbon steel and 0.45% carbon steel bar specimens which were cold drawn to cross-sectional reductions from 5 to 29% were measured. The cold drawing was carried out several times by the cross-sectional reduction of about 5% per pass. The residual stresses in the section of specimens after drawing were tensile at the outer part of the specimens, and compressive at the inner part of the specimens. The maximum residual stress at the outer part increased successively with the cross-sectional reduction to about 20%, and decreased over 20%. There are differences in the variation of the normal residual stress distribution with increasing cross-sectional reduction below and over at 20%. The textures in the outer and inner parts of these specimens were measured. The influence of the structure for the occurrence of residual stresses was discussed.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 54 (3), 336-345, 1990

    公益社団法人 日本金属学会

被引用文献 (3)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ