溶湯の直接圧延法によるクラッド板の製造

DOI Web Site Web Site

書誌事項

タイトル別名
  • Manufacture of Clad-plate with the Process of Direct-rolling of Molten Metals
  • ヨウトウ ノ チョクセツ アツエンホウ ニ ヨル クラッドバン ノ セイゾウ

この論文をさがす

説明

The manufacturing conditions and subsequent work conditions were investigated for the manufacuture of clad-plate of aluminium and its alloys with the process of direct-rolling of molten metals. The main results obtained were as follows:<BR>(1) In case of the alloys with a wide solidification range, the condition of junction between pure aluminium surface sheets and the core was good and became improved as the direct-rolling speed was decreased. In case of the alloys which showed the ripple mark defects in the surfaces, the surface sheets ruptured at a slower direct-rolling speed.<BR>(2) By the cold-rolling of clad-plates as the subsequent work, only the surface sheets were elongated and torn off from the core. By the hot-rolling, the junction between surface sheets and the core was complete and the desired quality of clad-sheets was obtained.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 34 (8), 775-779, 1970

    公益社団法人 日本金属学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ