- Effect of Germanium Additions on the Properties of New High Magnetic Permeability Alloy “Nimalloy” in the Nickel and Manganese System
- Ni-Mnケイ シン コウトウジリツ ゴウキン Nimalloy ノ トクセイ ニ オヨボス Ge テンカ ノ エイキョウ ニ ツイテ
- Effect of Germanium Additions on the Properties of New High Magnetic Permeability Alloy “Nimalloy” in the Nickel and Manganese System
この論文をさがす
抄録
Masumoto et al. previously discovered that alloys near in composition to Ni3Mn exhibited a high magnetic permeability when these alloys had an optimum degree of order, and named them “Nimalloy”. A great deal of works have since been carried out on the effects of additions of various elements on the properties of nickel-manganese alloys, and consequently the highest initial permeability of 76000 and the highest maximum permeability of 441000 have been obtained.<BR>In the present study additions of germanium to nickel-manganese alloys showed that the initial and maximum permeabilities of nickel-manganese alloys increased gradually at the beginning and then rapidly attained a maxima, and afterwards decreased gradually. The highest initial permeability of 15180 was obtained on the alloy of 77.89%Ni, 17.98%Mn and 4.13%Ge when cooled at a rate of 240°C/hr from 900°C and reheated at 400°C for 10 hr, and the highest maximum permeability of 167000 on the alloy of 78.27%Ni, 17.11%Mn and 4.62%Ge when cooled at a rate of 240°C/hr from 900°C and reheating at 400°C for 8 hr. The latter alloy shows a coercive force of 0.0046 Oe and a magnetic hysteresis loss of 12.58 erg/cm3/cycle for the maximum magnetic induction of 2000 G, and its electrical resistivity being 65.4 μΩ-cm at 20°C.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 33 (9), 1007-1011, 1969
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206484101504
-
- NII論文ID
- 130007336649
- 40018256821
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 8372135
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可