- Microstructures of a 3.5 GPa Grade Maraging Steel
- 3 5GPaキュウ マルエージング コウ ノ ビサイ ソシキ
この論文をさがす
抄録
Changes in hardness and microstructure during aging at 773 K (500°C) of a 3.5 GPa grade maraging steel having the concentration of 8%Ni-14%Mo-20%Co-58%Fe with or without pre-cold-working after quenching from 1623 K (1350°C) have been observed by transmission electron microscopy and electron diffraction. Results obtained are as follows:<BR>(1) The hardness increased rapidly after short time aging. In these specimens modulated structures have been observed. The wave length was several nano-meters and increased by pre-cold-working.<BR>(2) The wave length of modulated structures in over-aged specimens aged for 300 h was about 50 nm, and M2Mo (Laves phase) particles severel nano-meters in diameter precipitated densely in the Mo-enriched zones in the modurated structure in the in-situ manner. However, the contrast of modurated structure was indistinct, and increase of the wave length during aging was suppressed by pre-cold-working. Consequently, the dispersion of precipitated M2Mo particles was more uniform than that in the specimen without pre-cold-working.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 47 (1), 48-54, 1983
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206484336512
-
- NII論文ID
- 130007337054
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 2578083
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可