- Increase of Electrical Resistivity with Ordering of Fe-(50-80 at%)Pd Alloys
- Fe-(50~80at%)Pd合金の規則化に伴う電気抵抗の増加
- Fe 50 80atパーセント Pd
この論文をさがす
抄録
Electrical resistivity measurements, X-ray diffractometry and transmission electron microscopy of Fe-Pd alloys have been carried out. The electrical resistivity of 50-80 at%Pd alloys increases rapidly with ordering below the order-disorder transition temperature (Tc), while it is nearly constant in the disordered phase above Tc. Below Tc these alloys have the FePd superlattice (L10 type) in the range of 50-58 at%Pd and the FePd3 superlattice (L12 type) in the range of 63-77.5 at%Pd. All of the alloys below Tc are formed with long-range order. Fe-Pd ordered alloys are the first to show an increase in electrical resistivity associated with the formation of long-range order. It is suggested that the formation of superlattice of Fe-Pd system can be explained by the Brillouin Zone effect.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 51 (4), 285-291, 1987
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206484642048
-
- NII論文ID
- 130007337598
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 3133201
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可