- Electron Microstructure of the Aged Ti-8%Mn Alloy
- Ti-8パーセント Mn ゴウキン ノ ジコウザイ ノ デンシ ケンビキョウ ソシキ
この論文をさがす
抄録
In the Ti-8%Mn alloy brine quenched from 950°C, ω′ (which gives diffuse diffraction spots at the same positions as ω) and α″ (fcc martensite) phases besides retained β phase were observed by electron microscopy. In this report, the authors studied the structure change of these phases by aging treatment at 450°C and the structure of the precipitated ω. According to the result of the electron microscopic observation on the aged materials, ω′ grows to ω and α″ decomposes into α and β. The crystal structure of the ω phase is hexagonal and its c axis is parallell to ⟨111⟩β. It is observed that the precipitated ω phase has a rod shape which elongates along ⟨111⟩β and its longitudinal size is approximately 300 Å. The α phase is observed in the specimen aged for 60 min and it has Widmansttaten structure. The orientation relationship between β phase and α phase is [0001]α\varparallel[110]β.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 33 (2), 152-157, 1969
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206484647552
-
- NII論文ID
- 130007337608
- 40018256658
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 8371972
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可