- Strain Gage Factor and Electrical Properties of Fe-Cr-Co-W and Fe-Cr-Co-Mo Alloys
- Fe Cr Co Wケイ オヨビ Fe Cr Co Moケイ ゴウキン ノ テ
この論文をさがす
抄録
The gage characteristics such as the strain gage factor Gf, the electrical resistivity ρ, the temperature coefficient Cf and the thermo-electromotive force relative to copper Emf were investigated for Fe-15%Cr-5-40%Co+0-7%W and Fe-15%Cr-5-40%Co+0-7%Mo alloys cold-drawn by 30-99% reduction in cross-sectional area.<BR> Fe-Cr-Co-W and Fe-Cr-Co-Mo alloys are scarcely varied in Gf with the reduction in area. The values decrease with increasing Co content in the former quarternary alloys as previously reported for Fe-Cr-Co ternary alloys and show a maximum at 20%Co in the latter alloys. At more than 25%Co, the values of Gf in these quarternary alloys range from 4.0 to 4.1 and is slightly larger than those of the Fe-Cr-Co ternary alloys. On the other hand, the dependence of Gf on the W or Mo content becomes smaller with increasing Co content. Compared with other gage characteristics, the dependence of ρ, Cf and Emf on W content in the Fe-Cr-Co-W alloys and that of Cf on Mo content in the Fe-Cr-Co-Mo alloys are small as is the case with Gf. From the measurement of electrical resistivity at elevated temperatures up to 1273 K and X-ray diffraction analysis, it is clear that the micro-structures of both quarternary alloys in the cold-worked state consist of an α′ phase caused by the strain-induced transformation.<BR>Fe-14.3%Cr-28.6%Co-4.8%W and Fe-14.7%Cr-29.4%Co-2.0%Mo alloys cold-drawn by 98% reduction in area show the following values: In the case of the former alloy, Gf=4.1, ρ=0.93 μΩ·m, Cf=7.8×10−4 K−1 and Emf=+0.6 μV·K−1; in the latter alloy, Gf=4.1, ρ=0.86 μΩ·m, Cf=4.0×10−4 K−1 and Emf=+0.3 μV·K−1. Despite a rather poor workability of cold-rolling, it is relatively easy for these alloys to be cold-drawn into fine wires. Therefore, the alloys can be used as strain gage elements in load cells and micro-strain sensors, etc.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 51 (12), 1201-1208, 1987
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206484920832
-
- NII論文ID
- 130007338093
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 3167380
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可