The internal friction Q−1, and magnetic and mecanical properties were investigated as a function of Cr concentration in Ni-Co-Nb-Cr alloys containing 25, 45 or 65%Co and 3 or 5%Nb when furnace-cooled or water-quenched after heating at 1273 K for 7.2 ks. Measurements of the Q−1 and magnetic properties were carried out by an inverted torsion pendulum method and an automatic recording fluxmeter, and the mechanical properties were studied by using an Instron-type tensile testing machine.<BR>The maximum internal friction against the maximum shear strain-amplitude, Qmax−1, increased with Cr concentration, and the highest values of 59-91×10−3 were obtained for the alloys investigated. In the case of Ni-Co-Nb-Cr alloys with constant 3%Nb and 25, 45 and 65%Co, the Qmax−1 were highest at 3%Cr upon furnace cooling and 1%Cr upon water quenching, respectively. In the case of Ni-Co-Nb-Cr alloys with constant 5%Nb and 25, 45 and 65%Co, the highest values of Qmax−1 were obtained at 1%, 3% and 2%Cr upon furnace cooling and at 1%Cr upon water quenching, respectively.<BR>The coercive force Hc of the alloys decreased with the the increase in Cr concentration. The Hc of the alloys with high values of Qmax−1 increased with the increase in Co concentration; 0.051∼0.053 kA/m at 25%Co, 0.075∼0.11 kA/m at 45%Co and 0.10∼0.13 kA/m at 65%Co.<BR>Both the tensile strength and the yield strength of the alloys increased with increasing Cr concentration, while the elongation remained almost unchanged and showed fairly large values of 40∼60%.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 51 (11), 1093-1099, 1987
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206484944128
-
- NII論文ID
- 130007338137
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 3157732
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可