Fe-B-Si系アモルファス合金の構造緩和過程における電気抵抗の可逆的変化とメスバウアー分光

DOI Web Site Web Site 被引用文献3件

書誌事項

タイトル別名
  • Reversible Changes in Electrical Resistivity and Mössbauer Spectroscopy in Structural Relaxation of Amorphous Fe-B-Si Alloys
  • Fe B Siケイ アモルファス ゴウキン ノ コウゾウ カンワ カテイ ニ
  • Reversible Changes in Electrical Resistivity and Mössbauer Spectroscopy in Structural Relaxation of Amorphous Fe-B-Si Alloys

この論文をさがす

抄録

The structural relaxation process of amorphous Fe78B7Si15 and Fe82B13Si5 alloys has been studied by electrical resistivity measurements and Mössbauer spectroscopy. The topological distribution of first-neighbor iron atoms at an iron atom was changed and the average number of first-neighbor iron atoms increased during the change in topological short range order (TSRO) with irreversible changes of resistivity. Reversible changes of resistivity due to chemical short range order (CSRO) were observed in Fe78B7Si15 alloy which contained one kind of metallic atom. The resistivity decreased with increasing CSRO. The kinetics of CSRO in this alloy can be described as a log-normal distribution of relaxation times. The activation energy for the CSRO was estimated to be 222.0 kJ/mol from the resistivity measurement. This value is nearly equal to that for diffusion of Fe and Si atoms in Fe-based amorphous alloys. It is therefore likely that Fe and Si atoms play an important role in the CSRO of this alloy.

収録刊行物

被引用文献 (3)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ