- Effect of Preparatory-Deformation Temperature on High Temperature Shape Change of a Cu-Zn-Al Alloy
- Cu-Zn-Al合金の高温形状変化に及ぼす予備変形温度の影響
- Cu Zn Al ゴウキン ノ コウオン ケイジョウ ヘンカ ニ オヨボス ヨ
この論文をさがす
抄録
In a previous report, the authors showed that shape-changes in the temperature range 700∼1000 K occur during thermal cycles up to about 1000 K in a Cu-27.6 mass%Zn-3.8 mass%Al alloy which was deformed at room temperature after being quenched from the β phase region to 273 K. The amount of shape-change increases with increasing maximum temperature during the thermal cycles.<BR>In the present report, using a Cu-25.3 mass%Zn-3.9 mass%Al alloy, the effect of deformation temperature on the shape-change has been studied. The samples were deformed at temperatures from 77 to 670 K, using a die in a salt bath, an oil bath, etc. The maximum temperature of each thermal cycle is set at 1000 K. The results show that the amount of shape-change by the thermal cycle is constant for the deformation in a temperature range lower than about 300 K, increases for the deformation up to about 400 K and decreases for the deformation in a higher temperature range. No appreciable shape-change, however, can be detected at 670 K. In the case of the deformation at higher temperatures than 420 K, it was observed that the amount of shape-change decreases with increasing heating time before the deformation.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 51 (7), 694-699, 1987
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206485218048
-
- NII論文ID
- 130007338620
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 3145331
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可