1Cr-1Mo-1/4V鋼に析出するMo<SUB>2</SUB>C-V<SUB>4</SUB>C<SUB>3</SUB>炭化物

DOI Web Site Web Site
  • 小松 周一
    東京芝浦電気株式会社総合研究所金属セラミック材料研究所
  • 中村 新一
    東京芝浦電気株式会社総合研究所金属セラミック材料研究所
  • 中橋 昌子
    東京芝浦電気株式会社総合研究所金属セラミック材料研究所

書誌事項

タイトル別名
  • Mo<SUB>2</SUB>C-V<SUB>4</SUB>C<SUB>3</SUB> Carbides Precipitated in 1Cr-1Mo-1/4V Steel
  • 1Cr-1Mo-〓V鋼に析出するMo2C-V4C3炭化物
  • 1Cr 1Mo V コウ ニ セキシュツスル Mo2C V4C3 タンカブツ

この論文をさがす

抄録

H-shaped carbides precipitated in Cr-Mo-V steel were studied by electron microscopy and X-ray energy spectrometry. The results show that carbides consist of two different types, granular and needle-like carbides. The former carbide was V4C3 and the latter was Mo2C. The Mo2C precipitated on {111} habit planes of V4C3 with the orientation relationships (00.1)Mo<SUB>2C</SUB>\varparallel(\bar111)V<SUB>4C3</SUB> and [10.0]Mo<SUB>2C</SUB>\varparallel[110]V<SUB>4C3</SUB>. In this steel, various Mo2C-V4C3 carbides were observed. When V4C3 has a pair of the Mo2C needles, it is H-shaped, because the Mo2C needles grow in parallel on the opposite {111}V<SUB>4C3</SUB> planes such as (1\bar11)V<SUB>4C3</SUB> and (\bar11\bar1)V<SUB>4C3</SUB>. When V4C3 has two pairs of the needles, it shows a #-shaped feature because of the two paralleld pairs.<BR>The growing direction of the Mo2C in the matrix seemed to have some relevance to the extent of the misfit between Mo2C and matrix.<BR>It was also clarified by the creep rupture test that Mo2C-V4C3 carbides were thermally stable during the creep rupture test.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 43 (6), 485-491, 1979

    公益社団法人 日本金属学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ