高炭素鋼低温焼鈍線材の諸性質におよぼすパテンティング前の冷間加工の影響

DOI Web Site Web Site

書誌事項

タイトル別名
  • Effects of Cold-Drawing Prior to Patenting on the Mechanical Properties of High Carbon Steel Wire after Low Temperature Annealing
  • コウタンソ コウ テイオン ショウドン センザイ ノ ショ セイシツ ニ オヨボス パテンティング マエ ノ レイカン カコウ ノ エイキョウ

この論文をさがす

説明

Effects of prior cold drawing on the mechanical properties of 0.8%C steel, patented, cold drawn and then low temperature annealed, has been studied by tensile tests, torsion tests, Charpy impact tests and fatigue tests.<BR>The results of tensile tests after patenting show that specimens cold drawn prior to patenting (Specimen B) are stronger than those which were not cold drawn prior to patenting (Specimen A). Also, the pearlitic structure of specimen B is finer than that of specimen A. The austenite grain size of specimen A is larger than that of specimen B.<BR>After patenting, the specimens were cold drawn and low temperature annealed at 100°∼640°C. Specimen B is stronger than specimen A after these treatments as well as after patenting. Elongation and reduction in area of specimen A are larger than those of specimen B, but the number of torsion of specimen B is smaller than that of specimen A.<BR>Charpy impact results show that the absorbed energy of specimen B is larger than that of specimen A when both specimens were annealed at temperatures between room temperature and 250°C, but, when they were annealed at 300°∼400°C, this tendency becomes reversed.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 32 (3), 234-238, 1968

    公益社団法人 日本金属学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ