- Functional Features of Hard Tension/Compression Tester Developed for High Temperature Microscope and its Metallurgical Applications
- コウオン ケンビキョウヨウ ヒッパリ アッシュク シケンキ ノ トクセイ ト
この論文をさがす
抄録
A hard tension/compression tester has been constructed in the specimen holder of a high temperature microscope, without any interference with the functional features of the microscope including the side-entry goniostage. A noticeable advantage of the microscope was the in-situ observation of metallurgical phenomena at every stage of the load-elongation curves at high temperatures. The specific features are as follows:<BR>(1) The standard specimen for tension/compression test is 5 mm in gauge length, 2 mm in width and 0.5∼1 mm in thickness.<BR>(2) The maximum load is 100 kg.<BR>(3) The maximum stroke is 5 mm.<BR>(4) The cross head displacement speed is kept at the given value in six steps such as 0.025,0.020,0.015,0.010,0.005 and 0.0025 mm/s during elongation of specimens, independently of changing load.<BR>(5) The spring constant of the tester is estimated larger than 700 kg/mm or 7×106 N/m<BR>This tester was successfully applied to observing and recoding metallugical phenomena such as formation of the strain-induced martensite at 250°C in Fe-22%Ni alloy and the giant slip bands at 450°C during the serrated elongation of Cu-10 at%Al single crystal.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 43 (6), 563-568, 1979
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206485384448
-
- NII論文ID
- 130007338917
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 2055347
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可