- On the Nonferromagnetic Elinvar-Type Alloys in the Mn-Ni-W and Mn-Ni-W-Mo Systems
- Mn-Ni-Wケイ オヨビ Mn-Ni-W-Moケイ ヒキョウジセイ エリンバーカタ ゴウキン ニ ツイテ
この論文をさがす
説明
Measurements of Young’s modulus at −150∼400°C and of rigidity modulus, thermal expansion and hardness at room temperature have been carried out with Mn-Ni-W and Mn-Ni-W-Mo alloys subjected to various heat treatments and cold working. Young’s modulus vs temperature curves of the ternary and quarternary alloys slowly cooled after heating for 1 hr at 950°C showed distinct anomalous changes associated with antiferromagnetic\ ightleftarrowsparamagnetic transformation. Young’s modulus at room temperature does not show any great difference by the states of cold working and heat treatment, but it tends to increase with increasing manganese, tungsten or molybdenum content. The temperature coefficient of Young’s modulus is greatly affected not only by annealing, water quenching, cold working and reheating after water quenching or cold working but also by alloy composition. The positive temperature coefficient of Young’s modulus exist in a wide composition range, showing the appearance of the Elinvar property. The variation of rigidity modulus and its temperature coefficient with heat treatment, cold reduction rate and composition is quite similar to that of Young’s modulus and its temperature coefficient. The hardness shows a very complicatd change about 100 to 600 within the range of in Vickers hardness by the aforementioned treatments. The ternary and quarternary alloys have fairly good corrosion resistivity.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 37 (9), 1005-1010, 1973
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206485463296
-
- NII論文ID
- 130007339064
- 40018255388
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 7611035
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可