- New Nonmagnetic Elinvar-type Alloy “Pallagold” in the Pd-Au System
- Pd-Auケイ シン ヒジセイ エリンバーカタ ゴウキン Pallagold ニ ツイテ
- New Nonmagnetic Elinvar-type Alloy “Pallagold” in the Pd-Au System
この論文をさがす
抄録
Young’s modulus, rigidity modulus and thermal expansion in the palladium-gold system were measured at low and high temperatures after various heat-treatments and cold works. It has been found that the temperature coefficients of Young’s modulus and rigidity modulus of palladium-gold alloys annealed at 1000°C for 1 hr show a negative minimum value of −3.0×10−5 at a composition of 50% gold. However, the minimum turns to a positive value of 2.8×10−5 when heated at 360°C for 15 hr after water quenching from 1000°C or cold reducing of 96%. And the thermal expansion coefficient of palladium-gold alloys annealed at 1000°C for 1 hr has a minimum at composition of 48% gold. This minimum corresponds to the maximum temperature coefficient of Young’s modulus or rigidity modulus in the palladium-gold alloys. Moreover, the hardness of these alloys heated at 360°C for 15 hr after water quenching or cold working is about two times that in the annealed state. These alloys were named “PALLAGOLD” which is a abbreviation of palladium-gold alloy.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 33 (1), 121-125, 1969
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206485762816
-
- NII論文ID
- 40018256586
- 130007339596
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 8371900
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可