- Substructures Developed during Steady-State Creep of Fe-4.1 at%Mo Alloy at High Temperatures
- Fe 4 1 atパーセント Mo ゴウキン ノ コウオン クリープ ソシキ
この論文をさがす
抄録
Substructures developed during the steady-state creep of Fe-4.1 at%Mo bcc solid solution at 1100∼1200 K under 6∼40 MPa have been observed by transmission electron microscopy. The stress exponent, n, of the steady-state creep rates is 3.2±0.2. This result means that this alloy shows Class I behavior under the present creep condition.<BR>Sub-boundaries consisting of dislocation networks as well as rather homogeneously-distributed dislocations within subgrains are always observed. This fact suggests that the presence or the absence of sub-boundaries does not necessarily indicate the importance of viscous gliding of dislocations during steady-state creep deformation of solid solution alloys.<BR>Dislocation density within subgrains, ρG, and total dislocation density, ρT, increase with increase in the applied stress, σa : ρG∝σ1.5a and ρT∝σ1.3a. The length of sub-boundaries per unit area, L, which is reciprocally proportional to the subgrain diameter, increases with σa:L∝σ0.5a. The mean spacing of dislocations within sub-boundaries, l, decreases with σa:l∝σ−0.6a. The average internal stresses, ‾σi obtained by stress-transient dip-tests using a back-extrapolation technique are roughly proportional to \sqrtρG, \sqrtρT, and 1⁄l.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 43 (2), 135-140, 1979
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206485805696
-
- NII論文ID
- 130007339672
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 2042732
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可