- Damping Capacity of Cold-Worked Al-Ni Alloys
- レイカン カコウサレタ Al Ni ゴウキン ノ ゲンスイノウ
この論文をさがす
説明
The influence of cold working on the damping capacity and the mechanical properties was investigated for Al-Ni alloys containing 0.2 to 12%Ni. The logarithmic decrement δ and the rigidity modulus G were measured by an inverted torsion pendulum method, and the tensile strength σt by an Instron-typemachine.<BR>In both the furnace-cooled and water-quenched states the δ was increased in some degree by the Ni addition. By cold working after heat treatment, the δ became considerably higher with increasing reduction rate in area. The alloys cold-worked after furnace cooling was higher in δ than those cold-worked after water quenching; the Al-4%Ni alloy showed the highest δ value of 63×10−3 when cold-worked to 95% reduction rate in area. The increment in δ by cold working is considered to be due to a remarkable increase in density of dislocations and an action as pinning of a proper amount of compound Al3Ni (ε phase) on dislocation motion. Cold working after the heat treatment results in a decrease in G and an increase in σt. The G and σt both increased with increasing Ni concentration, irrespective of the heat treatment and the cold working that followed.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 50 (6), 590-593, 1986
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206486067840
-
- NII論文ID
- 130007340128
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 3082913
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可