Damping Capacity of Al-Ge Alloys

DOI Web Site Web Site 1 Citations

Bibliographic Information

Other Title
  • Al-Ge合金の振動減衰能
  • Al Ge ゴウキン ノ シンドウ ゲンスイノウ

Search this article

Abstract

The logarithmic decrement δ and the rigidity modulus G were investigated for heat-treated and cold-worked Al-Ge alloys containing 2 to 20 mass%Ge. The δ and G values were measured by an inverted torsion pendulum method.<BR>The δ values upon furnace cooling were somewhat higher than those upon water quenching, which were as low as 0.007. By cold working after heat treatment, the δ values of all alloys were increased considerably. With increasing Ge concentration, the δ upon cold working increased abruptly to 5 mass%Ge and then increased gradually. Moreover, in alloys cold worked after furnace cooling, the δ became higher than those cold-worked after water quenching.<BR>With increasing Ge concentration, the G increased, and cold working after heat treatment caused G to decrease. The ΔG effect increased abruptly up to 5 mass%Ge and then increased gradually, and high δ values were obtained in the alloys with a large ΔG effect.

Journal

Citations (1)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top