- Young’s Modulus of Single Crystals of Palladium at High Temperatures
- パラジウムタンケッショウ ノ コウオン ニ オケル ヤングリツ
- Young’s Modulus of Single Crystals of Palladium at High Temperatures
この論文をさがす
説明
Single crystals of palladium having a long length were prepared and their thermal expansions and Young’s moduli were measured over the temperature range 0° to 600°C by a dilatometer and by means of a vibrator-controlled oscillator system. From the measured values, the Young’s moduli in three principal orientations of the single crystals were calculated. The results show that the Young’s moduli at 20°C are 7.35, 13.77 and 19.44×105 kg/cm2 in the orientations of ⟨100⟩, ⟨110⟩ and ⟨111⟩ of the single crystal, respectively. The Young’s moduli in the ⟨100⟩ and ⟨110⟩ orientations of the single crystals decrease with increasing temperature, while the modulus in the ⟨111⟩ orientation increases to a maximum at about 250°C and then gradually decreases. The calculated value of the Young’s modulus for a polycrystal agrees fairly well with the measured value in the polycrystal specimen prepared by melting.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 32 (6), 529-532, 1968
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206486125824
-
- NII論文ID
- 130007340231
- 40018256489
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 8371803
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可