- Aso Setsuo
- Department of Materials Engineering and Applied Chemistry, Mining College, Akita University
-
- Tagami Michihiro
- Department of Materials Engineering and Applied Chemistry, Mining College, Akita University
-
- Goto Shoji
- Department of Materials Engineering and Applied Chemistry, Mining College, Akita University
Bibliographic Information
- Other Title
-
- Fe-15%Cr-C-B 4元系合金の状態図と凝固組織
- Fe 15パーセント Cr C B 4ゲンケイ ゴウキン ノ ジョウタイズ ト
Search this article
Abstract
Five kinds of phases were detected in the liquidus phase diagram of the Fe-15%Cr-C-B alloy system. Two types of peritectic reactions {L+M2B→M3(C, B) and L+M7(C, B)3→M3(C, B)} and four types of eutectic reactions {L→γ+M2B, L→γ+M3(C, B), L→γ+M23(C, B)6, L→γ+M7(C, B)3} were also detected on each liquidus phase boundary. The sum of carbon and boron concentrations in each boro-carbide was almost constant; that is, the sum was about 5.5% in M3(C, B), about 4.7% in M23(C, B)6 and about 7.5% in M7(C, B)3; however, the carbon and boron concentrations in each boro-carbide changed compensatory in these constant concentrations. In the M2B liquidus phase region, two types of boride were detected: one was a columnar boride with high boron content, which was identified as a M2B type boride, the other was a plate-like boride with low boron content, which was still unknown in this investigation. The conjugate relations of γ phase and the compound phase were in good agreement with the solidification structures.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 57 (4), 377-383, 1993
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001206489752832
-
- NII Article ID
- 130007340543
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 3826853
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed